Procolle MS high tack white - Sealant - Zep Industries

Procolle MS high tack white - Sealant - Zep Industries

One-component, fast- curing , very high initial adhesion sealant based on highly effective MS polymer , intended for flexible bonding and sealing of many materials.

Properties :

• Very fast adhesion : Very strong initial adhesion which hardens under the influence of humidity to give a durable elastic rubber.
• Effective : For bonding, mounting and sealing almost all (building) materials on almost all surfaces (smooth, porous and non-porous surfaces).
  Perfect adhesion to most materials such as raw metals (steel, zinc, aluminum), treated and varnished surfaces, wood and its derivatives, duroplast materials and thermoplastics (except PE, PP and PTFE), on mineral surfaces such as glass, etc.
• Convenient to use : No fixation or support required during treatment.
  Due to the high initial strength, support during curing is generally not necessary.
• Temperature range : After application, good temperature resistance from -40°C to +80°C continuously (up to +120°C peak).
• Resistance to weather and humidity : Good humidity and usual weather conditions.

Manual :

Surface preparation:

1. The surfaces to be glued or grouted must be clean, dry, free of dust or any greasy substance.
2. Store materials and work preferably in dry and heated rooms.

Working Temperature: +5°C to +30°C.

1. Compatibility and adhesion must be tested individually when applying to plastic, painted, lacquered or treated materials.

Bonding/sealing:

1. The mastic is deposited by extrusion of beads or by blocks in sufficient quantity between the materials to be sealed or glued.
2. The quantity to be deposited depends on the flatness of the supports to be assembled, the dimensions of the joints as well as the maximum expected deformation.
3. The display of the counter material or the smoothing of the cord should be done within the skin formation time (It is recommended not to exceed 10 minutes).
4. When gluing, apply pressure to obtain the desired joint thickness.
5. If the ratio of quantity of glue deposited to weight is sufficient, it is not necessary to keep the materials in contact using a fixing during the setting time.
6. For smoothing, use a spatula if necessary.
7. The speeds of formation of a skin on the surface and of polymerization depend on the thickness of the joint, the temperature and the humidity level of the air and the supports.
8. For application with a pneumatic gun, a pressure of 3 to 5 bars is recommended.

Conditioning :

310 g cartridge.